intergranular fracture是什么意思,intergranular fracture的意思翻译、用法、同义词、例句
常用词典
n. 晶粒间破裂
例句
Intergranular fracture with small fraction of transgranular was its character.
断裂以沿晶断裂为主,并具有一定的解理特征;
The composite displays the fracture features of the dimple and intergranular fracture.
复合材料的断裂形貌为韧窝加沿晶断裂。
The cracking of alloy with very low stress-corrosion resistance, welded and stored in open air for a long time, is caused by the welded stress and such a fracture is a typical intergranular fracture.
抗应力腐蚀性能低的合金焊接后,在大气中长期存放沿熔合线发生的开裂,是由焊接应力引起的,断口是典型的脆性沿晶断裂。
The results showed that the grain boundary cohesion become weaker and intergranular fracture became dominant with the increasement of superplastic deformation temperature.
结果表明,变形温度愈高,晶界结合强度愈低,沿晶断裂愈明显,晶界滑动愈易实现;
The void and intergranular fracture is developed due to the creep with the stress concentration at the defect tip at elevated temperature.
长期在应力集中作用下缺陷尖端处出现局部的蠕变和蠕变裂纹扩展,形成空洞和沿晶断裂的颗粒状断口。
This paper shows the results of a study of an intergranular fracture in bot low alloy steel castings, Poor ductility and low toughness are often associated with fracture mode.
对两种低合金铸钢的沿晶脆性断裂现象进行了研究,结果表明,两种脆化材料的断口均为沿晶脆性断裂。
High manganese steels undergo a ductile to brittle transition at low temperature, which is accompanied by a change in the fracture mechanism from dimple fracture to intergranular fracture.
高锰奥氏体钢随温度降低其断裂机制由韧窝状断裂转变到晶界断裂。
The deep and large cavities are formed on fracture surface and grain boundary sliding and intergranular fracture characteristic is obvious on the optimal superplastic deformation condition.
在最佳超塑性条件下,断口中形成了大而深的空洞,晶界滑动和晶间断裂特征明显。
Intergranular fracture. Fracture of polycrystalline materials by crack propagation along grain boundaries.
多晶材料裂纹沿着晶界扩展而断裂。
Because of the smaller grain of X70 pipeline steel, the typical intergranular fracture characteristics have not found.
由于X70管线钢的晶粒很细小,在碳酸盐溶液中的断口并没有呈现典型的晶间断裂冰糖状断口形貌。
The result shows that it was the typical intergranular fracture, and there were scrappy claw and tiny pore in the fracture of crystal face.
结果表明:弹性垫圈断口为典型的沿晶断裂,在断裂的晶面上有细小的爪状纹和微孔。 此为高强度钢氢脆断口的特征。
The material removing mechanism of 90% alumina is intergranular fracture caused by network cracks induced by impact.
氧化铝陶瓷材料的去除机理是冲击作用形成网状裂纹,导致材料晶间断裂;
Failure pattern of transgranular fracture and intergranular fracture depends on the intension of crystal.
裂纹尖端晶体强度影响穿晶和绕晶的破坏模式;
It is intergranular fracture when the volume content of Mo is lower, while intergranular fracture and transgranular fracture appear when the volume content of Mo is higher.
当Mo含量较低时主要为沿晶断裂,随着Mo含量的增加表现为沿晶断裂和穿晶断裂。
The fracture of the material was diverted from the manner of intergranular brittle fracture to the manner of intergranular brittle fracture with dimple gliding fracture.
材料的断裂方式由沿晶脆性断裂转变为沿晶脆性断裂和韧窝韧性断裂的混合断裂方式。
The fracture mode of the alloy in T6 state is transgranular shearing and intergranular dimple mixed fracture.
合金T6态的断裂方式为穿晶剪切和沿晶韧窝混合型断裂;
The gold is less evenly distributed in the ore in forms of natural gold and silver-gold, and occurring state are intergranular gold and fracture gold.
金矿物有自然金和银金矿,在矿石中分布很不均匀,以粒间金和裂隙金为主要赋存形式。
Fracture observation showed that the alloy exhibited brittle fracture with intergranular section and cleavage facet.
断口观察表明,含纳量较高的合金发生脆性断裂,断口为解理和沿晶混合型。
Rupture occurs near the bond zone. The characteristics of fracture are intergranular.
断裂发生在近焊缝处,断裂的特点是沿晶界的。
At the same time, the electric field lessenes percentages of intergranular delamination and increases transgranular fracture and microscopic plastic deformation.
同时,固溶电场减少合金的沿晶分层断裂比例,并增加穿晶断裂及微区塑性变形;
The results show that the main reason for the cracking was high temperature intergranular oxidation, with the fracture morphology being a typical intergranular cracking character.
结果表明,造成主蒸汽滤网开裂的主要原因是晶界高温氧化,断口呈典型的沿晶开裂特征。
Cassiterite is produced in the intergranular pore space or micro fracture and related to autometasomatism of late-post magmatic processes. Its mineralization temperature is 440-230℃.
锡石产于造岩矿物粒间隙和微裂隙中,与岩浆末期—期后自交代作用有关,锡矿形成温度为440~230℃。
It is pointed out that reservoir space of conglomerate is composed of primary intergranular pore, hole and fracture, secondary denudation pore and structural fracture.
指出,砾岩的储集空间为原生砾间孔、砾间洞、粒间缝、次生溶蚀孔和构造缝。
The fracture surface appeared intergranular crack, due to the oxide formed during tensile test.
拉伸过程中形成的氧化物夹杂成为裂纹源,断口表现为沿晶断裂。
The reservoir pore space mainly consists of intergranular pore, solution pore and fracture, dominated by residual intergranular pores and solution pores.
其储集空间主要分粒间孔、溶蚀孔和裂缝,以残余粒间和溶蚀孔为主。
In light of the fracture mechanics theory, the intergranular and cleavage wear characteristics of polycrystalline diamond (PCD) tool are analyzed firstly.
本文首先利用断裂力学的理论,分析了聚晶金刚石刀具切削过程中的沿晶和解理两种磨损特征及其形成过程。
The results show that the fracture for the spring results from intergranular crack strips induced by hydrogen on the subsurface because of an inappropriate grinding machining.
结果表明,此批弹簧断裂是由磨削加工不当在磨剂端面下亚表层产生了氢致沿晶开裂带,弹簧服役承载时在正应力的作用下发生了氢滞后脆性断裂。
网络扩展资料
intergranular fracture
词性
名词
定义
晶界断裂,是指沿晶界发生的金属或合金断裂。在材料科学中,晶界是相邻的晶粒之间的边界,晶界断裂是指在晶粒中发生的断裂现象。
发音
英式发音:[ˌɪntəˈɡranjʊlə(r)],美式发音:[ˌɪntərˈɡrænjʊlər]
用法
- The presence of intergranular fracture in a metal indicates that the metal has undergone significant stress or exposure to high temperatures.(金属中出现晶界断裂表明该金属已经承受了显著的应力或高温暴露。)
- Intergranular fracture can be prevented through proper heat treatment and alloying.(适当的热处理和合金化可以预防晶界断裂。)
解释
晶界断裂是一种材料破坏的形式,通常发生在金属或合金中。当金属或合金受到应力或高温影响时,晶粒之间的结构可能会受到损坏,导致晶界断裂。晶界断裂会导致材料的强度和韧性下降,因此在材料设计和制造过程中需要注意预防晶界断裂。
近义词
- Transgranular fracture(穿晶断裂)
反义词
- Ductile fracture(延性断裂)
fracture
词性
名词
定义
破裂,是指材料或物体因受到应力或冲击而破裂或断裂的现象。在材料科学中,断裂是指材料中的断开或裂纹。
发音
英式发音:[ˈfræktʃə(r)],美式发音:[ˈfræktʃər]
用法
- A fracture in the bone can be very painful and can take a long time to heal.(骨折可能非常疼痛,并且需要很长时间才能愈合。)
- The fracture in the metal was caused by a sudden impact.(金属中的断裂是由于突然的冲击引起的。)
解释
断裂是指材料或物体因受到应力或冲击而破裂或断裂的现象。断裂通常会导致材料或物体的结构和性能发生变化,因此在工程设计和制造过程中需要注意预防断裂。在材料科学中,断裂是指材料中的断开或裂纹,这些裂纹可能会导致材料的疲劳性能下降或材料失效。
近义词
- Break(破碎)
- Crack(裂纹)
反义词
- Integrity(完整性)
- Continuity(连续性)
英语单词大全 请记住链接:https://danci.yuesha.com/intergranular+fracture.html