stress corrosion cracking是什么意思，stress corrosion cracking的意思翻译、用法、同义词、例句

[力] 应力腐蚀裂痕

The role of hydrogen embrittlement in stress corrosion cracking has also been discussed.

文中还对氢脆在应力腐蚀开裂中的作用进行了讨论。

Through the discussion on the mechanism and effect factors of the stress corrosion cracking by sulfides, this paper expounds its harmfulness and proposes some measures to control it.

本文通过对硫化物应力腐蚀开裂的机理和影响因素的讨论，说明其危害性并提出了控制方法。

It has been proved that these cracks are caused by sulfide stress corrosion cracking(SSCC) through failure analysis and service environment survey.

通过失效分析和管道服役环境调查，证明开裂原因是管道服役期间发生硫化物应力腐蚀开裂（SSCC）。

Results show that both high temperature quenching and step quenching can apparently increase the stress corrosion cracking resistance K_(ISCC).

结果表明，高温淬火和分级淬火可使应力腐蚀断裂抚力K_（ISCC）值得到明显提高。

The results show that the early failure of the cooling pipe was caused by the stress corrosion cracking in the components.

结果表明，冷却水管发生早期失效是由于构件发生应力腐蚀开裂所致。

In this paper, we raise really available measures through the investigation, analysis, test and research about the stress corrosion cracking of pressure vessel for ammonia refrigerating equipments.

通过对氨制冷压力容器应力腐蚀开裂进行调查、分析、试验和研究，提出切实可行的对策措施。

The corrosion behavior of 2D12 alloy was evaluated including intergranular corrosion, exfoliation and stress corrosion cracking.

对不同规格2D12铝合金进行晶间腐蚀、剥蚀和应力腐蚀性能测定。

The examination and analysis reveal that the cracking of the plates is the result of stress corrosion cracking (SCC) caused by polythionic acid.

通过对隔板的检查和分析，判断隔板断裂属于连多硫酸引起的应力腐蚀开裂。

Using the NACE standard bent-beam test, the behavior of sulfide stress corrosion cracking(SSCC) of different microstructures for X70 grade pipeline steel was investigated.

采用三点弯曲法研究了不同组织类型的X70级管线钢的硫化物应力腐蚀开裂（S SCC）行为。

Accidents of liquid ammonia equipment used in petrochemical industry happen mostly due to stress corrosion cracking.

石油化工用液氨设备事故多数源自液氨应力腐蚀开裂。

Crack and shelling of coatings on underground pipeline is one of the main reasons for pitting corrosion and stress corrosion cracking of the pipeline .

埋地管道的涂覆层因损伤而开裂起翘，是引发其点蚀穿孔和应力腐蚀断裂的主要原因之一。

It is found that there are solidification cracking within argon arch welding joint between heat exchange pipe and pipe plate and stress corrosion cracking on its surface.

对某台加热器发生泄漏的部位进行了金相、扫描电镜检查，检查出换热管与管板的氩弧焊缝内部存在结晶裂纹且表面存在应力腐蚀裂纹。

Various mechanisms of hydrogen-induced cracking and stress corrosion cracking have been reviewed.

本文对各种氢致开裂和应力腐蚀机理进行了评述。

The effect of high-temperature pre-precipitation on the microstructure, age hardening and stress corrosion cracking of 7A52 alloy has been investigated.

研究了高温预析出对7A52合金组织、时效硬化和应力腐蚀断裂的影响。

It was concluded that the Cl ion in the oil glue resulted in stress corrosion cracking of the pure copper tube.

结果表明，紫铜管渗漏系腐蚀引发裂纹所致，而涂在铜管表面的油胶中的氯离子是引起紫铜管应力腐蚀开裂的主要因素。

There are some factors which influence the characteristics of initiation and propagation of stress corrosion cracking and corrosion fatigue cracking in high-strength steel in a watery environment.

影响高强度钢在水介质中的应力腐蚀和腐蚀疲劳裂缝萌生和扩展特性的因素甚多。

Brittle fracture is a stress corrosion cracking phenomenon which occurs in high voltage composite insulators. Previous studies all focused on the source of the corrosion medium, e. g. the acid.

脆断是高电压复合绝缘子发生的应力腐蚀断裂现象，国内外的研究基本集中在“腐蚀”介质酸的来源上。

The discrepancies of stress corrosion cracking susceptibility between different types of steel, base matal and welds are analyzed.

材料因素方面主要分析了三种不同种类的钢以及同一钢种母材和焊缝的应力腐蚀敏感性的差异。

The stress corrosion cracking(SCC) of carbon steels in aqueous alkali was studied by electrochemical technique, stress corrosion test under constant load and repassivation test.

本工作通过电化学，恒载荷应力腐蚀和再钝化试验，对碳钢在碱溶液中的应力腐蚀破裂进行了研究。

A kind of testing machine used to study stress corrosion cracking of materials in natural environment and special environment was introduced, such as toxic atmosphere and corrosion medium.

介绍了一种可以用于研究材料在自然环境及特定环境（如有毒有害气氛、各种腐蚀介质等）下应力腐蚀性能的便携式拉伸应力腐蚀试验装置。

Stress corrosion cracking problem of concrete beams with crack is studied in this paper.

本文研究了带裂纹混凝土梁的应力腐蚀断裂问题。

Stress corrosion cracking of an X60 pipeline steel in soil containing water has been investigated using slow strain rate test.

用光滑试样慢应变速率拉伸法研究了X60管线钢在含水土壤中的应力腐蚀。

The rupture reasons of tube joint weld of the stainless steel pressure meter are analyzed. It is characteristic of stress corrosion cracking and inter granular fracture.

分析了不锈钢压力表管接头焊缝开裂的原因，认为此种开裂具有应力腐蚀开裂、沿晶断裂特征。

Pitting corrosion and crevice corrosion in catalyst deposit zone and corrosion deposit zone can also induce stress corrosion cracking.

催化剂沉积区和腐蚀产物沉积区产生的点蚀和缝隙腐蚀会诱发应力腐蚀开裂的产生。