tempering temperature是什么意思,tempering temperature的意思翻译、用法、同义词、例句
常用词典
[机] 回火温度
例句
On the other hand, the MIM steel specimens were tempered at various temperatures in order to evaluate effect of tempering temperature on fatigue property.
另一方面,为了评估回火温度对疲劳性能的影响,将MIM钢试样于不同温度下进行了回火。
According to the tempering temperature and hardness curve, the redistribution of residual stress is associated with the transformation of residual austenite.
由回火温度与硬度变化曲线证实,残余应力重新分布是与残余奥氏体转变相关联。
Effect of tempering process on the microstructure and mechanical properties of XCQ16 steel was investigated. The results show that XCQ16 steel present a wider tempering temperature range.
研究了不同回火温度对XCQ16钢微观组织和力学性能的影响,试验结果表明:XCQ16钢具有较宽的回火温度范围。
The results show that quenching temperature, tempering temperature and holding time are determining factors.
结果表明: 加热温度、 回火温度、 保温时间起着决定性作用;
Influences of normalizing temperature and tempering temperature on mechanical properties and microstructure of ZG310-570 cast steel were investigated.
研究了正火温度和回火温度对ZG310-570铸钢组织和力学性能的影响。
The effect of following factors on thermal fatigue resistance of GJW50 steel-bonded tungsten carbide, such as, austenitizing temperature, tempering temperature and hardness, has been studied.
研究了奥氏体化温度,回火温度及硬度对GJW50碳化钨钢结硬质合金热疲劳抗力的影响。
The effects of matrix strength on three-point bent fatigue strength for the nitriding parts made from the nitrided steel have been studied by changing tempering temperature during pre-treatment.
通过改变预处理回火温度,研究了基体强度对氮化钢渗氮件三点弯曲疲劳强度的影响。
The sizes and kinds of carbides and their distribution are mainly dependent on the tempering temperature.
碳化物的形态、种类、分布主要取决于回火温度。
At the quenching temperature (900~1100℃)when the tempering temperature is lower than 450℃, the amount of residual austenite has slight variation.
在试验淬火温度范围(900~1100℃)内450℃以下回火,奥氏体含量变化不明显;
The results show that the quenching temperature, tempering temperature and speed have great influences on the tensile strength, yield strength.
结果表明,淬火温度、回火温度和运行速度对抗拉强度、屈服强度影响很大。
When tempering temperature is below 700℃, the strength decreases slightly with the tempering temperature rises.
回火温度低于700℃时,钢板强度随温度的增加缓慢降低;
The results showed that the main factors, which affected dimension changing of GCr15, included residual austenite content, tempering temperature and tempering time.
根据模型模拟结果表明,影响轴承钢硬化层尺寸稳定性的主要因素是残余奥氏体的含量和回火温度以及回火时间。
The influences of quenching and tempering temperature on microstructure and mechanical properties of medium-carbon-low-alloy wear-resistant cast steel were investigated.
研究了淬火和回火温度对中碳低合金耐磨铸钢组织和力学性能的影响。
The results show that the microstructure of 45 steel is substantially softened, the wear resistance rapidly decreases with the tempering temperature rising.
结果表明,随回火温度的升高,45钢组织的大幅度软化导致耐磨性明显下降。
Fatigue strength of the MIM specimens declined with increasing tempering temperature.
MIM钢试样的疲劳强度随着回火温度升高而减低。
When tempering temperature further heightens, he hardness descends gradually.
当回火温度进一步升高时,硬度逐渐降低。
The cause of fracture is related with tempering temperature, machining defects on the surface and chemical composition of the fracture bolt.
主要原因与热处理回火温度、表面加工缺陷以及材料化学成分有关。
With increasing tempering temperature, the retained austenite decreases.
回火温度升高,其残余奥氏体量逐渐减少。
The Influence of quenching temperature and tempering temperature on mechanical properties and microstructure of ZG310-510 cast steel was studied.
研究了淬火温度和回火温度对ZG310-510铸钢组织和力学性能的影响。
It is found that the steel resistances to fatigue crack growth increase with the rising of the tempering temperature when it is higher than the second hardening peak temperature.
发现高于二次硬比峰温度回火时,此钢的疲劳裂纹扩展阻力随回火温度升高而增加。
Influences of aging treatment, quenching temperature and tempering temperature on structure and property of medium-chromium cast iron were investigated.
研究了稀土元素及热处理对中铬半钢冲击疲劳性能的影响。
The other reasons were lower tempering temperature and slower temper cooling rate.
回火温度偏低及回火冷却速度偏缓等,是零件冲击韧度不足的另一原因。
The results show that the best quenching temperature is 850 ℃, the hardness is not significantly changed(50~53 HRC)through different quenching and tempering temperature.
结果表明,试验钢的最佳淬火温度为850℃,试验钢经不同温度淬火、低温回火后,钢的硬度变化并不显著,在50~53HRC之间;
Having studied the relationship between tempered hardness and tempering temperature for hardened carbon steels, a tempering behaviour model is set up between hardness and temperature.
研究了淬硬钢回火硬度与回火温度的关系,建立了回火硬度与回火温度关系的回火效应模型。
The structure homogenization as well as UTS and elongation is related to tempering temperature time, interlayer agent etc.
其组织的均匀程度与抗拉强度、延伸率一样与回火温度、时间及中间层合金的成份有关。
网络扩展资料
Tempering
解释: Tempering是指将热处理过的金属再次加热后冷却的过程,以改变其硬度、韧性和其他机械性能。Tempering常用于钢铁制品的制造和加工中,以使其具有所需的物理特性,如强度和耐久性。
例句:
- The steel blade was tempered to increase its toughness. (这把钢刀被回火处理以增加其韧性。)
- The metal parts were tempered to improve their durability. (这些金属零件被回火处理以提高其耐久性。)
用法: Tempering是一个名词,常用于描述金属加工中的处理过程和方法。可以用作动词,表示进行回火处理。
近义词: Quenching、Annealing、Hardening
反义词: Softening、Weakening
Temperature
解释: Temperature是指物体的热度,通常用来描述物体的热量和热状态。温度可用不同的温标进行测量,如摄氏度、华氏度和开氏度。
例句:
- The water temperature was too high for swimming. (水温对游泳来说太高了。)
- The temperature in the room was too low, so I turned up the heat. (房间的温度太低了,所以我打开了暖气。)
用法: Temperature是一个名词,常用于描述物体的热状态和热度。可以用作动词,表示测量温度或调节温度。
近义词: Heat、Degree、Warmth
反义词: Cold、Freezing
英语单词大全 请记住链接:https://danci.yuesha.com/tempering+temperature.html